Forming Low Stress Joints Using Thermal Compress Bonding

ABSTRACT

A method of forming a bump structure includes providing a first work piece including a dielectric layer having a top surface; placing a second work piece facing the first work piece; placing a heating tool contacting the second work piece; and heating the second work piece using the heating tool to perform a reflow process. A first solder bump between the first and the second work pieces is melted to form a second solder bump. Before the second solder bump solidifies, pulling the second work piece away from the first work piece, until an angle formed between a tangent line of the second solder bump and the top surface of the dielectric layer is greater than about 50 degrees, wherein the tangent line is drawn at a point where the second solder bump joins the dielectric layer.

This application is a divisional of U.S. patent application Ser. No.12/841,882 filed Jul. 22, 2010 entitled “Forming Low Stress Joints UsingThermal Compress Bonding,” which applications are hereby incorporatedherein by reference in their entireties.

TECHNICAL FIELD

This disclosure relates generally to integrated circuit manufacturingprocesses, and more particularly to forming low-stress joints usingthermal compress bonding.

BACKGROUND

Integrated circuits are formed on semiconductor wafers, which are thensawed into semiconductor chips. The semiconductor chips are then bondedonto package substrates. FIGS. 1 through 3 illustrate cross-sectionalviews of intermediate stages in a conventional bonding process.Referring to FIG. 1, package substrate 100 is provided, and bond pads108 are at the surface of package substrate 100. Chip 102 is picked upand flipped over, with solder bumps 104 at a surface of chip 102 facingdown. Flux 106 is also applied on solder bumps 104.

Next, as shown in FIG. 2, chip 102 is placed on package substrate 100,with solder bumps 104 being placed against bond pads 108. Packagesubstrate 100 and chip 102 then go through a reflow process, duringwhich package substrate 100 and chip 102, and solder bumps 104 areheated. The resulting bonded structure is shown in FIG. 3. Due to theweight of chip 102 and solder bumps 104, solder bumps 104, when melted,are crushed, and width W1 of solder bumps 104 increases.

One of the problems found in the conventional bond structures is thatcracking often occurs in solder bumps 104 after the bonding process,particularly near wherein solder bumps 104 join solder resists 112 and114. In addition, due to the increase in width W1 of solder bumps 104,the spacing between neighboring solder bumps 104 need to be increased toprevent solder bumps 104 from shorting with each other.

SUMMARY

In accordance with one aspect, a method of forming a bump structureincludes providing a first work piece including a dielectric layerhaving a top surface; placing a second work piece facing the first workpiece; placing a heating tool contacting the second work piece; andheating the second work piece using the heating tool to perform a reflowprocess. A first solder bump between the first and the second workpieces is melted to form a second solder bump. Before the second solderbump solidifies, pulling the second work piece away from the first workpiece, until an angle formed between a tangent line of the second solderbump and the top surface of the dielectric layer is greater than about50 degrees, wherein the tangent line is drawn at a point where thesecond solder bump joins the dielectric layer.

Other embodiments are also disclosed.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the embodiments, and the advantagesthereof, reference is now made to the following descriptions taken inconjunction with the accompanying drawings, in which:

FIGS. 1 through 3 illustrate cross-sectional views of intermediatestages in a conventional bonding process;

FIGS. 4 through 8B are cross-sectional views of intermediate stages inthe manufacturing of a bond structure in accordance with variousembodiments; and

FIG. 9 illustrates spacing S (FIG. 8) between neighboring solder bumpsas a function of pull up heights, and heights H of solder bumps as afunction of the pull up heights.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

The making and using of the embodiments of the disclosure are discussedin detail below. It should be appreciated, however, that the embodimentsprovide many applicable inventive concepts that can be embodied in awide variety of specific contexts. The specific embodiments discussedare merely illustrative, and do not limit the scope of the disclosure.

A novel thermal compress bonding (TCB) process is provided. Theintermediate stages of manufacturing various embodiments areillustrated. Throughout the various views and illustrative embodiments,like reference numbers are used to designate like elements.

FIG. 4 illustrates a cross-sectional view of work piece 26. In anembodiment, work piece 26 is a package substrate or an interposer, whichdoes not have active devices such as transistors therein. In alternativeembodiments, work piece 26 is a device die having active devices such astransistors (not shown) therein. Metal pads 28 may be formed in workpiece 26, and exposed through an opening in solder resist 30, which isformed of a dielectric material. Solder bumps 32 are formed on the topsurface of, and are electrically coupled to, metal pads 28. Solder bumps32 may include portions over dielectric layer 30, and portions extendinginto the openings in dielectric layer 30. In alternative embodiments,bumps 32 are non-reflowable metal bumps such as copper pillar bumps.

FIGS. 5A and 5B illustrate work pieces 40, which may be device dies(chips) comprising active devices (not shown) therein, wherein theactive devices may be transistors. Alternatively, work pieces 40 may beinterposers, package substrates, or the like. Metal pads 42 may beformed in work pieces 40. Dielectric layer 44 is formed over metal pads42, and may be formed of polyimide, silicon oxide, silicon nitride, orthe like. In an embodiment, as shown in FIG. 5A, solder bumps 46 areformed on the top surfaces of, and are electrically coupled to, metalpads 42. In alterative embodiments, as shown in FIG. 5B, under-bumpmetallurgies (UBMs) 47 are formed, with each of UBMs 47 including aportion extending into the respective opening in dielectric layer 44,and a portion over dielectric layer 44. Solder bumps 46 are formed onthe top surfaces of the respective UBMs 47. UBMs 47 may comprise atitanium layer and a copper layer on the titanium layer, for example,although different metallic materials may be used. In an embodiment,bumps 46 are solder bumps, although they can be other type of bumps suchas copper pillar bumps. However, at least one, and may be both, of metalbumps 32 (FIG. 4) and 46 are solder bumps. In the following illustratedexemplary embodiments, metal bumps 32 and 46 are all solder bumps.

Referring to FIG. 6, work piece 40 is picked up, flipped over, andplaced onto work piece 26. Metal bumps 32 are in contact with solderbumps 46. Next, as shown in FIG. 7, a bonding is performed. Heating tool60 is placed over and contacting work piece 40, and may apply a downwardforce (symbolized by arrow 62) to work piece 40, so that metal bumps 32and 46 are pressed against each other to prevent work piece 40 fromslipping. Heating tool 60 heats work piece 40, and the heat is conductedto, and cause the reflow of, solder bumps 32 and 46. The resultingsolder bumps formed of the combined solder bumps 32 and 46 are referredto as solder bumps 66. During the melting of solder bumps 32 and 46,downward force 62 may be, or may not be, applied.

Referring to FIGS. 8A and 8B, after the reflow to form solder bumps 66and before solder bumps 66 solidify, heating tool 60 applies an upwardforce, as symbolized by arrow 68, so that the height H of solder bumps66 is increased, and horizontal size W2 of solder bumps 66 is reduced.The application of the upward force may be achieved, for example, byforming a vacuum in air duct 67 in heating tool 60 to suck work piece 40up. The pulling up of work piece 40 is continued until angles α1 and α2are higher than certain values (such as 50 degrees), as will bediscussed in detail in subsequent paragraphs. The temperature of heatingtool 60 is then reduced until solder bumps 66 solidify. The bondingprocess is then finished. After the bonding, underfill 70 is filled intothe gap between work pieces 26 and 40.

In the resulting structure as shown in FIGS. 8A and 8B, at the jointswhere solder bumps 66 join dielectric layer 30, solder bumps 66 havetangent lines 72, which form angle α1 with horizontal surface 30 a(which is in a horizontal plane) of dielectric layer 30. Each of tangentlines 72 may have one end meeting a joint of solder bumps 66 anddielectric layer 30, wherein the joint may be the corner of dielectriclayer 30, which corner is where horizontal surface 30 a intercepts asidewall of dielectric layer 30. Similarly, at the joints where solderbumps 66 join dielectric layer 44, solder bumps 66 have tangent lines76, which form angles α2 with horizontal surface 44 a (which is in ahorizontal plane) of dielectric layer 44. In the embodiment wherein UBMs47 are formed in work piece 40, as shown in FIG. 8B, angles α2 may beconsidered as between tangent lines 76 and horizontal surface 47 a ofUBMs 47. In an embodiment, angles α1 and α2 are greater than about 50degrees, greater than about 60 degrees, or even greater than about 75degrees. It is known that increased angles α1 may result in the decreasein the stress at the corners where solder bumps 66 join dielectric layer30, where the stress in solder bumps 66 is often the highest near thecorners. Accordingly, the cracking in solder bumps 66 caused by thestress is reduced. Similarly, the increased angles α2 may result thedecrease in the stress at the corners where solder bumps 66 joindielectric layer 44 or UBMs 47, and hence the reduction in the crackingin solder bumps 66. It is observed that when height H of solder bumps 66is increased, angles α1 and α2 also increase. Accordingly, by pulling upwork piece 40 in the reflow process, angles α1 and α2 may increase, andthe cracking in solder bumps 66 may be reduced.

The increase in height H also results in spacing S between neighboringsolder bumps 66 to be increased. Assuming solder bumps 66 in some samplebond structures are pulled up from an original height H equal to 64 μm,and a pull up height is used to measure the increase in height H fromthe original height of 64 μm, then in FIG. 9, line 84 may be used toillustrate spacing S (FIGS. 8A and 8B) as a function of the pull upheights, and line 82 may be used to illustrate height H of solder bumps66 as a function of the pull up height. It is observed that both spacingS and height H increase substantially linearly with the increase in thepull up height. In other words, by pulling up work piece 40 in thereflow process, spacing S may be increased linearly with the increase insolder bump height H. Accordingly, the risk of shorting is reduced whensolder bump height H is increased, and solder bump density may beincreased. The possibility of cracking in solder bumps 66 is alsoreduced.

Although the embodiments and their advantages have been described indetail, it should be understood that various changes, substitutions andalterations can be made herein without departing from the spirit andscope of the embodiments as defined by the appended claims. Moreover,the scope of the present application is not intended to be limited tothe particular embodiments of the process, machine, manufacture, andcomposition of matter, means, methods and steps described in thespecification. As one of ordinary skill in the art will readilyappreciate from the disclosure, processes, machines, manufacture,compositions of matter, means, methods, or steps, presently existing orlater to be developed, that perform substantially the same function orachieve substantially the same result as the corresponding embodimentsdescribed herein may be utilized according to the disclosure.Accordingly, the appended claims are intended to include within theirscope such processes, machines, manufacture, compositions of matter,means, methods, or steps. In addition, each claim constitutes a separateembodiment, and the combination of various claims and embodiments arewithin the scope of the disclosure.

What is claimed is:
 1. A method comprising: placing a second work pieceover a first work piece; placing a heating tool over and contacting thesecond work piece; heating the second work piece using the heating toolto melt a solder region between the first work piece and the second workpiece; when the solder region is melted, pulling up the second workpiece to increase a height of the solder region from a first height to asecond height greater than the first height; and cooling the solderregion, wherein after the step of cooling, the first work piece and thesecond work piece are bonded to each other through the solder region. 2.The method of claim 1, wherein the after the cooling, the solder regionhas the second height.
 3. The method of claim 1, wherein the second workpiece is pulled up through a vacuum formed in the heating tool.
 4. Themethod of claim 1 further comprising, before pulling up the second workpiece, pressing the second work piece against the first work piece. 5.The method of claim 1, wherein after the step of placing the second workpiece over the first work piece, a first solder bump in the first workpiece is in contact with a second solder bump in the second work piece,and wherein the solder region comprises solder from the first solderbump and the second bump.
 6. The method of claim 1, wherein after thestep of placing the second work piece over the first work piece, a firstbump in the first work piece is in contact with a second bump in thesecond work piece, and wherein the solder region comprises solder from afirst one of the first and the second bumps, and wherein a second one ofthe first bump and the second bump is a non-reflowable bump.
 7. Themethod of claim 1, wherein the second work piece is pulled up until anangle formed between a tangent line of the solder region and a topsurface of a surface dielectric layer in the first work piece is greaterthan about 50 degrees, and wherein the tangent line is drawn startingfrom a joint of the solder region and the surface dielectric layer. 8.The method of claim 7, wherein the angle is greater than about 60degrees.
 9. The method of claim 8, wherein the angle is greater thanabout 75 degrees.
 10. A method comprising: placing a second work pieceover a first work piece, wherein the first work piece comprises: a firstdielectric layer having a top surface; and a first solder bump having afirst portion over the first dielectric layer, and a second portionextending into the first dielectric layer, and wherein the second workpiece comprises a second solder bump at a surface, and wherein the firstand the second solder bumps contact each other; placing a heating toolcontacting the second work piece; heating the second work piece usingthe heating tool to melt the first and the second solder bumps to form athird solder bump; and before the third solder bump solidifies, pullingup the second work piece, until an angle formed between a tangent lineof the second solder bump and the top surface of the dielectric layer isgreater than about 50 degrees, wherein the tangent line is drawnstarting from a joint of the third solder bump and the dielectric layer.11. The method of claim 10, wherein the angle is greater than about 60degrees.
 12. The method of claim 11, wherein the angle is greater thanabout 75 degrees.
 13. The method of claim 10, wherein the first workpiece is a package substrate, and the second work piece is a device die.14. The method of claim 10, wherein at a joint of the third solder bumpand the second work piece, an additional tangent line of the secondsolder bump forms an additional angle greater than about 50 degrees witha horizontal surface of the second work piece.
 15. A device comprising:a first work piece comprising a dielectric layer having a top surface; asecond work piece; and a solder bump bonding the first work piece to thesecond work piece, wherein a tangent line of the solder bump drawnstarting from a joint of the solder bump and the dielectric layer formsan angle with the top surface of the dielectric layer, and wherein theangle is greater than about 50 degrees.
 16. The device of claim 15,wherein the angle is greater than about 60 degrees.
 17. The device ofclaim 15, wherein the angle is greater than about 75 degrees.
 18. Thedevice of claim 15, wherein the first work piece is a package substrate.19. The device of claim 15, wherein the first work piece is a devicedie.
 20. The device of claim 15, wherein at a joint where the solderbump joins the second work piece, an additional tangent line of anadditional solder bump at a surface of the second work piece forms anadditional angle greater than about 50 degrees with a major surface ofthe second work piece.